Our quartz glass optical windows are resistant against high temperature and pressure and can be applied mainly in such fields as special light sources, optical instrument, optical electronics, military equipment, metallurgy, semi-conductor, and optical communications. Their experimental temperature is 1200 degrees and softening temperature 1730 degrees. Detailed parameters are given as follows: 1．JGS1( Extreme UV optical quartz glass) It is a high-purity optical quartz glass made by oxyhydrogen flame melting. Its satisfactory UV light transmission performance surpass all the other glass types in particular in the shortwave UV zone and can achieve a 90% transmission rate at the wavelength of 185nm. Hence it is an ideal choice for applications in the wavelength range of 185-2500nm. 2．JGS2 (UV optical quartz glass) It is an optical quartz glass made by oxyhydrogen flame melting and is suggested for applications in the wavelength range of 220-2500nm. 3． JGS3 (Infrared quartz glass) It has a good performance of infrared light transmission with a transmittance of over 85%. It is recommended for applications in the wavelength range of 260-3500nm

Quartz glass characteristics

Table 1.
Mechanical Property			Reference Value
Density			2.2g/cm3
Compressive Strength			1100Mpa
Bending Strength			67Mpa
Tensile Strength			48Mpa
Poisson's Ratio			0.14～0.17
Elastic Modulus			72000Mpa
Shearing Modulus			31000Mpa
Mohs Hardness			5.5～6.5
Table 2.
Mechanical Property			Reference Value
Deformation Point			1280℃
Softening Point			1780℃
Annealing Point			1250℃
Specific Heat(20～350℃)			670J/kg.℃
Thermal Conductivity(20℃)			1.4W/m.℃
Refractive Index			1.4585
Coefficient of thermal expansion			5.5×10-7cm/cm.℃
Hot work temperature			1750～2050℃
The temperature for a short time			1300℃
The temperature for a long time			1100℃
Table 3.
Electrics Property			Reference Value
Resistivity			7×107Ω.cm
Dielectric Strength			250～400Kv/cm
Dielectric Constant			3.7～3.9
Dielectric absorption coefficient			<4×104
Dielectric loss coefficient			<1×104